Effect of Nb content on the phase composition,densification, microstructure,and mechanical properties of high-entropy boride ceramics

Dense high-entropy (Hf,Zr,Ti,Ta,Nb)B₂ ceramics with Nb contents ranging from 0 to 20 at% were produced by a two-step spark plasma sintering process. X-ray diffraction indicated that a single-phase with hexagonal structure was detected in the composition without Nb. In contrast, two phases with the same hexagonal structure, but slightly different lattice parameters were present in compositions containing Nb. The addition of Nb resulted in the presence of a Nb-rich second phase and the amount of the second phase increased as the Nb content increased. The relative densities were all >99.5 %, but decreased from ～100 % to ～99.5 % as the Nb content increased from 0 to 20 at%. The average grain size decreased from 13.9 ± 5.5 μm for the composition without Nb additions to 5.2 ± 2.0 μm for the composition containing 20 at% Nb. The reduction of grain size with increasing Nb content was due to the suppression of grain growth by the Nb-rich second phase. The addition of Nb increased Young’s modulus and Vickers hardness, but decreased shear modulus. While some Nb dissolved into the main phase, a Nb-rich second phase was formed in all Nb-containing compositions.     

Effect of atmosphere control on magnetic properties of CaO-Al2O3-SiO2-Fe3O4 glass ceramics

The influences of atmosphere during processes of melting and heat treatment, heat treatment temperature, Fe₃O₄ content and basicity on the magnetic properties of magnetite-based glass ceramics were investigated. For sample containing 20 % Fe₃O₄ melted in different atmospheres, the highest saturation magnetisation was realized in 20vol% air + 80 vol% Ar, due to the fact that ratio of Fe³⁺ to Fe²⁺ in melt obtained in this atmosphere was close to 2. However, it was found that the coercivity of glass ceramics was not affected by the melting atmosphere. A high sintering temperature led to the decrease of saturation magnetisation and the increase of coercivity. As increasing Fe₃O₄ content, the main crystal phase transformed from CaSiO₃ to CaFe_0.6Al_1.3Si_1.08O₆ and finally to magnetite phase, accompanied by the increase of saturation magnetisation and coercivity. In addition, the increase of basicity caused the decrease of saturation magnetisation and the increase of coercivity.     

Constructing magnetically recoverable CdS/CaFe2O4 P–N heterojunctions for enhanced photoelectrochemical properties towards H2 evolution reaction

A novel CdS/CaFe₂O₄ (CS/CFO) heterogeneous p-n junction was created by thermal deposition of CaFe₂O₄ nanoparticles on CdS rods. The CS/CFO hetero-structured photocatalysts exhibited increasingly efficient visible light harvesting compared to the bare CdS. The CS/CFO composites also presented higher photocurrent and slower decay of photoluminescence, suggesting a better separation of the photo-generated electrons and holes. The photocatalytic H₂ evolution quantity on the optimized CS/CFO composite from water in the presence of ethanol was up to 2200 μmol after 3-h visible light illumination, which is more than twice that of the pristine CdS. The chemical interaction between CdS and CaFe₂O₄ was confirmed by the shifts in the XPS peaks, which made it possible for the charge carriers to transfer across the p-n junction interface. This research highlights the importance of forming an interfacial p-n heterojunction between two semiconductors for efficient charge separation and improved photocatalytic performance.     

Microstructural,mechanical properties and strengthening mechanism of DLP produced β-tricalcium phosphate scaffolds by incorporation of MgO/ZnO/58S bioglass

The inherent brittleness of bioceramics restricts their applications in load-bearing implant, although they possess good biocompatibility and bioactivity. ZnO, MgO and 58S bioglass (BG) were incorporated as additives to further improve the mechanical properties and biocompatibility of β-TCP and ZnO/MgO/BG-β-TCP composite scaffolds were manufactured via digital light processing (DLP). The composite with the best comprehensive performance was selected for degradation behavior and biocompatibility evaluation. The effects of different proportions of ZnO/MgO/BG on mechanical strength were analyzed and ZnO0·5/MgO1/BG2-β-TCP (ZMBT) samples exhibited superior mechanical strength. The improvement by 272% and 99% respectively was achieved in fracture toughness and compressive strength with the optimal recipe. The enhancement effect is realized through phase transition, alterative sliding actions and transgranular fracture to effectively prevent the load transfer combining the functions of bioglass and metal oxide. ZMBT scaffolds exhibited a more desirable pH environment and an enhanced ability of apatite-mineralization formation, meanwhile Si⁴⁺, Mg²⁺ and Zn²⁺ were gradually released from scaffolds. Furthermore, in vitro evaluation indicated that ZMBT scaffolds presented not only excellent cell attachment, proliferation, alkaline phosphatase (ALP) activity, but they up-regulated osteogenic gene (ALP, OCN, Runx2). These results suggest that the addition of ZnO/MgO/BG to DLP-printed β-TCP scaffolds offer a smart strategy to fabricate porous scaffolds with conspicuously better biological and physicochemical properties including compressive strength, bioactivity, osteogenesis and osteogenesis-related gene expression. Metal-oxide and BG synergistically enhanced the mechanical and biological properties which make the ZMBT scaffolds a strong candidate for bone repair applications.     

The activation of furfuryl alcohol polymerization by oxygen and its enhanced mechanical properties

The effect of oxygen and additional oxygen providers on furfuryl alcohol polymerization was investigated through chemical analyses and mechanical evaluation. NMR, UV–vis, Fourier transform infrared, and gas chromatography–mass spectrometry (GC–MS) results suggested that atmospheric oxygen and the further addition of an oxygen source functioned as an activator for the entire network polymerization. Interestingly, the construction of a conjugated structure on the furan linear chain, which is key to three-dimensional cross-linking, also appears to be accelerated in the presence of oxygen. Furthermore, the introduction of oxygen providers into the curing system successfully enhanced the mechanical properties of the cured furan resin.     

CrN和CrN/Ag涂层的真空高温摩擦磨损性能*

为改善涂层在真空、高温等苛刻条件下的摩擦学性能，利用中频直流磁控溅射技术在硅片和316L不锈钢上沉积了CrN和CrN/Ag涂层，利用扫描电镜、透射电镜和X射线衍射仪对涂层的成分及相结构进行了表征，通过划痕测试仪、纳米压痕仪和摩擦磨损试验机测试了涂层的力学及摩擦学性能。结果表明：添加Ag元素以后，CrN/Ag涂层硬度及承载能力有所减小，但结合强度增加；真空高温环境下CrN与CrN/Ag涂层摩擦因数随温度升高呈下降趋势，其中CrN涂层通过软化镀层减小剪切强度和阻力，从而减小摩擦因数，CrN/Ag涂层主要通过高温产生的热驱动力诱导表面Ag润滑膜的形成来减小摩擦因数；CrN涂层依靠自身剪切特性参与摩擦，而CrN/Ag涂层在真空高温下具有自润滑和持续润滑性能，作为自润滑零部件具有潜在的应用价值。     

Mechanical Properties of Single-Layer Diamond Reinforced Poly(vinyl alcohol) Nanocomposites through Atomistic Simulation

Low-dimensional carbon nanostructures are ideal nanofillers to reinforce the mechanical performance of polymer nanocomposites due to their excellent mechanical properties. Through molecular dynamics simulations, the mechanical performance of poly(vinyl alchohol) (PVA) nanocomposites reinforced with a single-layer diamond – diamane is investigated. It is found the PVA/diamane exhibits similar interfacial strengths and pull-out characteristics with the PVA/bilayer-graphene counterpart. Specifically, when the nanofiller is fully embedded in the nanocomposite, it is unable to deform simultaneously with the PVA matrix due to the weak interfacial load transfer efficiency, thus the enhancement effect is not significant. In comparison, diamane can effectively promote the tensile properties of the nanocomposite when it has a laminated structure as it deforms simultaneously with the matrix. With this configuration, the interlayer sp³ bonds endows diamane with a much higher resistance under compression and shear tests, thus the nanocomposite can reach very high compressive and shear stress. Overall, enhancement on the mechanical interlocking at the interface as triggered by surface functionalization is only effective for the fully embedded nanofiller. This work provides a fundamental understanding of the mechanical properties of PVA nanocomposites reinforced by diamane, which can shed lights on the design and preparation of next generation high-performance nanocomposites.     

Characterization of barium titanate reinforced acrylonitrile butadiene rubber composites for flexible electronic applications: influences of barium titanate content

The aim of this study was to develop high dielectric constant flexible polymers with a highly efficient and cost‐effective approach using acrylonitrile butadiene rubber (NBR) as the polymer matrix and barium titanate (BT) as the high dielectric constant filler. The BT powder was synthesized with a solid‐state reaction and was characterized using a particle size analyzer, XRD, SEM and Fourier transform infrared spectroscopy. NBR/BT composites were fabricated using an internal mixer with various BT loadings up to 160 phr. The influence of BT loading on the cure characteristics and mechanical, dynamic mechanical, thermal, dielectric and morphological properties was determined. The incorporation of BT in the NBR matrix shortened scorch time and increased delta torque. The mechanical properties, thermal stability and dielectric constant were greatly improved and increased with BT loading. The results suggest that the reinforcement effect was achieved due to strong hydrogen bonding or polar–polar interactions between NBR matrix and BT filler. This is further corroborated by the good dispersion of BT filler in the NBR matrix observed with SEM imaging. These findings can be applied to produce high‐performance dielectric elastomers. © 2020 Society of Industrial Chemistry     

Effects of (Li0.5Sm0.5)/W co-substitution and sintering temperature on the structure and electrical properties of ultrahigh Curie temperature piezoceramics,Ca0.92(Li0.5Sm0.5)0.08Bi2Nb2-xWxO9

With co-substitution of (Li_0.5Sm_0.5) at A site and W at B site, the electrical properties of modified Ca_0.92(Li_0.5Sm_0.5)_0.08Bi₂Nb_2-xW_xO₉ [(CLS)BN-xW, x = 0, 0.015 and 0.03] piezoceramics with ultrahigh Curie temperature (T_C) of > 930 °C were enhanced dramatically. The increased resistivity induced by the co-substitution ensure them to be polarized under an enough high field. Combined with the increase of spontaneous ferroelectric polarization (P_S), the significant enhancements in the piezoelectric, dielectric and ferroelectric properties can be obtained in the composition x = 0.015. Furthermore, the piezoelectric activity (d₃₃) and bulk resistivity (ρ_b) of (CLS)BN-0.015 W can be further enhanced at an appropriate sintering temperature. This optimum composition sintered at 1170 °C shows ultrahigh T_C of ～948 °C, d₃₃ of ～17.3 pC/N and ρ_b of ～6.9 MΩ cm at 600 °C, which are comparable to those of the reported high-temperature Aurivillius piezoceramics with T_C > 850 °C.